Materials Table
The table below presents the more common alloys used by Smalley Steel Ring Company.
| Material |
Material
Thickness
(in) |
Minimum
Tensile
Strength
(psi) |
Shear
Strength
(psi) |
Maximum
Recommended
Operating Temp.4
(°F) |
Modulus of
Elasticity
(psi) |
|
Carbon Steel
|
Oil Tempered
SAE 1070 - 1090 |
.006 - .014 |
269,000 |
153,000 |
250 |
30 X 106 |
| .0141 - .021 |
255,000 |
145,000 |
| .0211 - .043 |
221,000 |
126,000 |
| .0431+ |
211,000 |
120,000 |
Hard Drawn
SAE 1060 - 1075 |
.006 - .030 |
230,000 |
130,000 |
| .0301 - .110 |
181,000 |
103,000 |
| .1101 - .220 |
156,000 |
89,000 |
|
302 Stainless Steel
|
| AMS-5866 |
.002 - .022 |
210,000 |
119,000 |
400 |
28 X 106 |
| .0221 - .047 |
200,000 |
114,000 |
| .0471 - .062 |
185,000 |
105,000 |
| .0621 - .074 |
175,000 |
100,000 |
| .0741 - .089 |
165,000 |
94,000 |
| .0891 - .085 |
155,000 |
88,000 |
|
316 Stainless Steel
|
| ASTM A3131 |
.002 - .023 |
195,000 |
111,000 |
400 |
28 X 106 |
| .0231 - .048 |
190,000 |
108,000 |
| .0481 - .061 |
175,000 |
99,000 |
| .0611+ |
170,000 |
97,000 |
|
17-7 PH/C Stainless
|
Condition CH900
AMS-5529 |
|
240,0002 |
137,0002 |
650 |
29.5 X 106 |
|
A-286
|
| ASMS-5810 |
|
180,0002 |
105,0002 |
1000 |
31 X 106 |
|
INCONEL5 Alloy X-750
|
Spring Temper
AMS-56993 |
|
220,0002 |
125,0002 |
700 |
31 X 106 |
NO. 1 Temper
"Rc 35 Maximum"
AMS-56991,3 |
|
136,000 REF |
77,000 |
700 |
NO. 1 Temper
AMS-5698 |
|
155,0002 |
88,0002 |
1000 |
| INCONEL5 Alloy 718 |
| AMS-55961 |
|
180,0002 |
102,0002 |
1300 |
29.6 X 106 |
|
ELGILOY5
|
| AMS-58761,3 |
≤ .004 |
300,0002 |
171,0002 |
800 |
30 X 106 |
| .0041 - .019 |
290,0002 |
165,0002 |
| .0191 - .025 |
280,0002 |
159,0002 |
| .0251 - .100 |
270,0002 |
154,0002 |
|
Beryllium Copper
|
Temper TH02
ASTM B1971 |
|
185,0002 |
128,0002 |
400 |
18.5 X 106 |
|
|
NOTE: Additional materials available include
Phosphor Bronze, C-276, 410 Stainless Steel, MONEL5 K-500, MONEL5 K-400, Waspaloy and others. Please consult Smalley Engineering for further details.
1 Referenced for chemical composition only.
2 Values obtained after precipitation hardening.
3 Conforms to NACE Standard MR-01-75.
4 Exceeding these temperatures will cause increased relaxation. Consult Smalley Engineering for High Temperature applications.